The vapor pressure of each of the niobium-zinc compounds was measured as a function of temperature. The kinetics of formation of the niobiumzinc compounds on pure niobium from zinc vapor were investigated, and oxidation tests were made on several coatings applied with zinc vapor. The mechanisms involved and the kinetics of the removal of interstitial impurities from niobium by the niobium-zinc compounds were also studied. Further studies of the effects of alloying elements added to the zinc bath used to coat niobium by the dip process confirmed that small amounts of nickel and aluminum in the proper combination are beneficial. (Author).

Progress made in applying advanced techniques and structural concepts to the problem of strengthening the Group VI-A metals, Cr, Mo, and W, is examined. At low temperatures, T/Tm

This publication documents Proceedings of the Symposium on Metal lurgy and Technology of Refractory Metal Alloys, held in Washington, D.C. at the Washington Hilton Hotel on April 25-26, 1968, under sponsorship of the Refractory Metals Committee, Institute of Metals Division, of the Metallurgical Society of AIME, and the National Aeronautics and Space Administration. The Symposium presented critical reviews of selected topics in refractory metal alloys, thereby contributing to an in-depth understanding of the state-of-the-art, and establishing a base line for further research, development, and application. This Symposium is fifth in a series of conferences on refractory metals, sponsored by the Metallurgical Society of AlME. Publications issuing from the conferences are valuable technical and historical source books, tracing the evolution of refractory metals from early laboratory alloying studies to their present status as useful engineering materials. Refractory metals are arbitrarily defined by melting point. A 0 melting temperature of over 3500 F was selected as the minimum for this Symposium, thus excluding chromium and vanadium, which logically could be treated with other refractory metals in Groups VA and VIA of the periodic table. The Refractory Metals Committee is planning reviews of chromium and vanadium in subsequent conferences.

This report summarizes the information generated since the middle of 1961 on the chemical, physical, and mechanical properties of refractory metals that are coated with oxidation-resistant coatings of advanced-experimental or commercial status. It is a supplement to DMIC Report 162, Coatings for the Protection of Refractory Metals from Oxidation, dated November 24, 1961. Recent data on specific silicide- and aluminide- type coatings for columbium, molybdenum, tantalum, and tungsten and their alloys reflect general advances in coating quality and performance, understanding of the behavior of coated systems, and more complete realization of the problems associated with the use of coated hardware.